Mill and Scrubber Linings

The Mill and Scrubber Linings a huge role in the cement industry now,it is very helpful for us to improve work efficiency and skill level.
1. Alloy: 15%Cr.
2. The Mill and Scrubber Linings are cleaned, sandblasted with a nice surface without any obvious visual defects that can avoid the normal working of the castings.
3. Hardness: more than HRC60;

4. Microstructure: Fine Martensite + Carbide + retained Austenite(≤6%)

The Combined Self-fastened Boltless Ni Hard Liners

It includes two parts,high wear resistance boltless plates, and highly expandable riveting plates,which are self-fastened and strengthened to withstand impact from mill balls.

Our Photos for Mill and Scrubber Linings:

  • Mill and Scrubber Linings
  • Mill and Scrubber Linings
  • Mill and Scrubber Linings
AS2074 HBW C Si Mn P S Cr Ni Mo Cu
AS2074 L2A ≤410 0.45-0.55 ≤0.75 0.5-1.0 ≤0.04 ≤0.04 0.8-1.2 - - -
AS2074 L2B ≤410 0.55-0.65 ≤0.75 0.5-1.0 ≤0.04 ≤0.04 0.8-1.5 - 0.2-0.4 -
AS2074 L2C ≤410 0.70-0.90 ≤0.75 0.5-1.2 ≤0.04 ≤0.04 1.3-2.4 - 0.2-0.4 -
Specification:
According to drawings, heat resistance, surface treatment requirement, Various types of 2D or 3D drawings are acceptable, etc.

Double-Media Quenching Chromium-Molybdenum Alloy Steel Series

We specially design the material for ball mill liners in mines, coal-fired power plants and cement plants,etc..

With our special double media quenching process,the material can not only achieve ideal hardness (HRC48~55) but also ideal toughness value (AK30~100J).

It can completely meet the requirement of liners of large and middle size ball mills at home and abroad.

The match of Middle Chrome Liners and High Chrome Cast Balls has been the typical model in coal mills and cement mills.Meanwhile, the material is applicable to the teeth plates,armored plates and hammers of crushers and excavator, bucket teeth.

Pearlitic Chromium-Molybdenum Alloy Steel Series

The Pearlitic Chromium Molybdenum Alloy Steel Liners are widely used in AG Mill,SAG Mill and Ball Mills.

Hardness: HB310-375 (equivalent to HRC33-42)
Impact resistant Value: Ak≥60J (60×10×10mm) in normal ambient temperature.

We can produce pearlitic Cr-Mo steel as per AS2074 Gr. L / 2B.

High Chrome White Iron Series

High Chrome white iron we can produce include 15%Cr, 18%Cr, 20%Cr and 26%Cr.
Under same working condition,the wear performance of High Chrome mill liners is four times of that of high manganese steel liners and twice of that of low Chrome alloy steel liners.

Meanwhile, we can produce high Chrome castings as per AS2027, ASTM A532 and BS4844.

Customer-made Mill Liners

In addition to our patented Boltless Mill Liners, we can produce liners as per the request of customers.

So far, we have been the regular suppliers of mill liners Now, we have supplied steel caps inserted in rubber lifters for SAG mills and AG mills to some mines in Australia and New Zealand.

Cost effective:
Integrated production from mold-making to post-processing is completed in our own factory. 
This can effectively reduce the manufacturing cost.
We have first rate production line, the most professional staff, and the advanced equipment and inspection method for casting. 
super quality,competitive price and strict delivery time.
Chemistry Standard for Mill and Scrubber Linings:

Standard Specification for Cr-Mo Alloy Steel:

Reference Standard

Nominal Chemical Composition (W%)

C

Si

Mn

P

S

Ni

Cr

Mo

AS 2074/L2A

0.45-0.55

≤0.75

0.50-1.00

≤0.04

≤0.04

0.80-1.20

AS 2074/L2B

0.55-0.65

≤0.75

0.50-1.00

≤0.04

≤0.04

0.80-1.50

0.2-0.4

AS 2074/L2C

0.70-0.90

≤0.75

0.50-1.20

≤0.04

≤0.04

1.30-2.40

0.2-0.4

ZG42Cr2Si2MnMo

0.38-0.48

1.5-1.8

0.8-1.2

≤0.04

≤0.04

1.8-2.2

0.2-0.6

ZG45Cr2Mo

0.40-0.48

0.8-1.2

0.4-1.0

≤0.04

≤0.04

≤0.5

1.7-2.0

0.8-1.2

ZG30Cr5Mo

0.25-0.35

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG40Cr5Mo(FED-4A)

0.35-0.45

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG50Cr5Mo

0.45-0.55

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG60Cr5Mo

0.55-0.65

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

FMU-29

0.25-0.45

0.3-1.0

0.6-1.5

≤0.04

≤0.04

6.0-8.0

0.2-0.4

FMU-11

0.90-1.30

0.3-1.0

0.6-1.5

≤0.04

≤0.04

11.0-13.0

0.3-0.5

FMU-13

0.80-1.30

0.4-1.2

0.8-1.5

≤0.04

≤0.04

11.0-13.0

0.4-0.8

FMU-14

1.60-2.00

0.4-1.2

0.8-1.5

≤0.04

≤0.04

11.0-13.0

0.6-1.0

Q: Can you produce according to the samples?
A: Yes, we can produce by your samples or technical drawings. We can build the molds and fixtures.

Q: What kinds of products do you offer?
A: We mainly produce various high alloy steel castings, such as mill liners, jaw crusher spare parts, jaw plates, cone crusher spare parts, Crusher Blow Bars, Crusher Hammers, etc.

Q: What kind of materials are using for the products?
A: We supply all kinds of high alloy steel castings, including manganese steel castings, high manganese steel, nickel hard castings, chromium molybdenum alloy steel, high chromium white iron castings, etc.

Q: What is the maximum weight of a single piece that can be cast, and what is your daily processing capacity?
A: The weight of a single piece that can be cast at one time is 30 tons. The production capacity is 150 tons/working day.

Q: What is your sample policy?
A: We can supply the sample if we have ready parts in stock, but the customers have to pay the sample cost and the courier cost.

Q: What is the Warranty for our products ?
A: If any quality problems on our side occurred in this period , we will take on the shipping cost and replacement.

Q: How to give inquiry?
A: Step 1, please tell us what weight ,dimension, material do you need please.
Step 2, Better help to provide the drawing with above-mentioned details please.
Step 3, when we have enough details, we may quote accordingly.

Q: What is the delivery time of your products?
A: It depends on the inventory availability.If items needed are in stock, the delivery time would be within 7 work days, but if not the delivery time would be around 30 work days.
We will send working schedule of your order each week.
The detailed inspection picturesion by email.

Q:  Do you test all your goods before delivery?
A: Yes, we have 100% test before delivery

Q: If your product has inferior quality or quality problem after we use them what happens next?
A: First, you have to provide us photos of the problem part and also provide photos of the use.
If it is indeed a quality problem of the product itself, we would offer compensation to you and also figure out solutions to avoid this kind of quality problem in the future.
If the problem is caused by clients, we would provide the technical suggestions to avoid same problems.

Q: Do you support drop shipping?
A: Yes, your drop shipping is aviable.

Q: Transportation?
A: Transported by DHL, UPS, EMS, Fedex, Air freight, Sea freight.

Q:  How do you make our business long-term and good relationship?
A:1. We keep good quality and competitive price to ensure our customers benefit ;
2. We respect every customer as our friend and we sincerely do business and make friends with them, no matter where they come from.

If you have interest, please do not hesitate to contact me.
Pls send the drawing,technical requirements to us by email.
Looking forward to receiving your inquiry and reply.
Thank you.

Feedback form contact with us
Product Catalog