Lifter Bars

Name: Cr-Mo Alloy Steel Casting Lifter Bars
Material:Cr-Mo alloy steel
Material Grade: AS 2074/L2A, AS2074/L2B, AS2074/L2C, ZG45Cr2Mo, ZG30Cr5Mo.
Dimensions:Based on drawings
Hardness:≥HRC60
Heat-treatment:Queching+Tempering
Certification:ISO 9001:2018
Surface treatment:Shot Blasting
Service:OEM ODM
Quality promise:GB/AS
Techinique:Sand casting/Lost foam casting
AK(J/CM2):>20
Surface Finish: Appro.Ra100
Size Tolerance: as per CT13
Microstructure: Fine Martensitic + Carbonate + Retained Austenitic less than 5%
Application: Chute Liners + Hopper Liners + Wear Plates
Cr & Mo casting block part will be compounded with rubber material, and then used in SAG mill.

Our Photos for Lifter Bars for SAG Mill:

  • Lifter Bars
  • Lifter Bars
  • Lifter Bars
Cr-Mo Alloy Steel Casting Lifter Bars in general refers to a kind of casting steel with the chromium content at 4-6%, the carbon content at 0.8-1.2%.
Its distinctive feature is to adopt multivariate alloy design. It increases carbide content in the medium carbon alloyed steel, through increasing the Cr & Mo content, the strong carbide forming elements, so as to improve its heat-resisting, wear-resisting performance.

As a result, its high strength, strong toughness and good wear resistance properties represent the relatively high level of metal wear resistant materials.

Specification:
According to drawings, heat resistance, surface treatment requirement, Various types of 2D or 3D drawings are acceptable, etc.
Cost effective:
Integrated production from mold-making to post-processing is completed in our own factory.
This can effectively reduce the manufacturing cost.
We have first rate production line, the most professional staff, and the advanced equipment and inspection method for casting.
super quality,competitive price and strict delivery time.

Standard Specification for Cr-Mo Alloy Steel:

Reference Standard

Nominal Chemical Composition (W%)

C

Si

Mn

P

S

Ni

Cr

Mo

AS 2074/L2A

0.45-0.55

≤0.75

0.50-1.00

≤0.04

≤0.04

0.80-1.20

AS 2074/L2B

0.55-0.65

≤0.75

0.50-1.00

≤0.04

≤0.04

0.80-1.50

0.2-0.4

AS 2074/L2C

0.70-0.90

≤0.75

0.50-1.20

≤0.04

≤0.04

1.30-2.40

0.2-0.4

ZG42Cr2Si2MnMo

0.38-0.48

1.5-1.8

0.8-1.2

≤0.04

≤0.04

1.8-2.2

0.2-0.6

ZG45Cr2Mo

0.40-0.48

0.8-1.2

0.4-1.0

≤0.04

≤0.04

≤0.5

1.7-2.0

0.8-1.2

ZG30Cr5Mo

0.25-0.35

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG40Cr5Mo(FED-4A)

0.35-0.45

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG50Cr5Mo

0.45-0.55

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

ZG60Cr5Mo

0.55-0.65

0.4-1.0

0.5-1.2

≤0.04

≤0.04

≤0.5

4.0-6.0

0.2-0.8

FMU-29

0.25-0.45

0.3-1.0

0.6-1.5

≤0.04

≤0.04

6.0-8.0

0.2-0.4

FMU-11

0.90-1.30

0.3-1.0

0.6-1.5

≤0.04

≤0.04

11.0-13.0

0.3-0.5

FMU-13

0.80-1.30

0.4-1.2

0.8-1.5

≤0.04

≤0.04

11.0-13.0

0.4-0.8

FMU-14

1.60-2.00

0.4-1.2

0.8-1.5

≤0.04

≤0.04

11.0-13.0

0.6-1.0

Q: Can you produce according to the samples?
A: Yes, we can produce by your samples or technical drawings. We can build the molds and fixtures.

Q: What kinds of products do you offer?
A: We mainly produce various high alloy steel castings, such as mill liners, jaw crusher spare parts, jaw plates, cone crusher spare parts, Crusher Blow Bars, Crusher Hammers, etc.

Q: What kind of materials are using for the products?
A: We supply all kinds of high alloy steel castings, including manganese steel castings, high manganese steel, nickel hard castings, chromium molybdenum alloy steel, high chromium white iron castings, etc.

Q: What is the maximum weight of a single piece that can be cast, and what is your daily processing capacity?
A: The weight of a single piece that can be cast at one time is 30 tons. The production capacity is 150 tons/working day.

Q: What is your sample policy?
A: We can supply the sample if we have ready parts in stock, but the customers have to pay the sample cost and the courier cost.

Q: What is the Warranty for our products ?
A: If any quality problems on our side occurred in this period , we will take on the shipping cost and replacement.

Q: How to give inquiry?
A: Step 1, please tell us what weight ,dimension, material do you need please.
Step 2, Better help to provide the drawing with above-mentioned details please.
Step 3, when we have enough details, we may quote accordingly.

Q: What is the delivery time of your products?
A: It depends on the inventory availability.If items needed are in stock, the delivery time would be within 7 work days, but if not the delivery time would be around 30 work days.
We will send working schedule of your order each week.
The detailed inspection picturesion by email.

Q:  Do you test all your goods before delivery?
A: Yes, we have 100% test before delivery

Q: If your product has inferior quality or quality problem after we use them what happens next?
A: First, you have to provide us photos of the problem part and also provide photos of the use.
If it is indeed a quality problem of the product itself, we would offer compensation to you and also figure out solutions to avoid this kind of quality problem in the future.
If the problem is caused by clients, we would provide the technical suggestions to avoid same problems.

Q: Do you support drop shipping?
A: Yes, your drop shipping is aviable.

Q: Transportation?
A: Transported by DHL, UPS, EMS, Fedex, Air freight, Sea freight.

Q:  How do you make our business long-term and good relationship?
A:1. We keep good quality and competitive price to ensure our customers benefit ;
2. We respect every customer as our friend and we sincerely do business and make friends with them, no matter where they come from.

If you have interest, please do not hesitate to contact me.
Pls send the drawing,technical requirements to us by email.
Looking forward to receiving your inquiry and reply.
Thank you.
Feedback form contact with us
Product Catalog