Cement Mill Liner


  • Minimum Order Quantity: 1 piece

  • Price: USD1.8~2.5/kg
  • Delivery time: 7-30 days

Minimum Order Quantity:1 piece
Price: USD1.8~2.5/kg
Delivery time: 7-30 days
Cement Mill Liner for Shot Blast Machines, Chutes, Clinker Silo,Port Machinery and Ball Mills.
This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.
These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining.
Heat treatment shall be done.
The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.

Shape: Flat Plate, Arc Plate, Waved Plates, Corrugated Plates.
Bolted Plates: one-hole, two-holes, three holes, four holes, oval – hole.
Quality Level: As per National Standard & International Standards.
Production Process: Sand Process with proper heat-treatment(quenching and tempering) process to achieve ideal hardness and impact value.

Photos for Cement Mill Liner:

  • Cement Mill Liner
  • Cement Mill Liner
  • Cement Mill Liner
Cement Mill Liner Application:
  • Armed plates for clincker silo in cement plants.
  • Wear plates for chutes, material bunkers for port machinery.
  • Material hoppers in steel mills.
  • High abrasion plates for material bin for port maachinery.
  • Wear plates for coal hoppers.
Cement Mill Liner Special Features :
  1. We make Cr-Mo Alloy steel and high Cr white iron castings with Sodium Silicate Sand Process and Resin Sand Process.
  2. Our supply finished alloy steel castings with heat-treatment and machining process.
  3. We can produce Alloy Cr-Mo Steel and White Iron castings as per GB/T26651, GB/T 8263-1999, AS2074, AS2027, DIN 1695,
    AISI, ASTM, JIS G 5153, NF A32401, BS4844.
  4. Our can recommend suitable material grades of wear parts for you as per your specific working condition.
  5. Design of wear plates & Chute Liners. Width and length of wear plates determines hole pattern, regardless of thickness.
  6. Material Selection of Wear Plates & Chute Liners.
Cement Mill Liner Material Grade:
  1. Martensitic Cr Mo AlloySteel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo): Hardness: ≥HRC48, Impact value: ≥25J.
  2. High Cr white iron (BTMCr15Mo, BTMCr20Mo, BTMCr26Mo): Hardness: ≥HRC56, Impact value: ≥5J.
  3. Ni-hard White Iron: AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630 AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630.

1. High Cr white iron:

ISO 21988/JN/ HBW C Si Mn P s Cr Ni Mo Cu
HBW555XCr13 555 1.8-3.6 1 0.5-1.5 0.08 0.08 11-14 2 3 1.2
HBW555XCr16 555 1.8-3.6 1 0.5-1.5 0.08 0.08 14-18 2 3 1.2
HBW555XCr21 555 1.8-3.6 1 0.5-1.5 0.08 0.08 18-23 2 3 1.2
HBW555XCr27 555 1.8-3.6 1 0.5-1.5 0.08 0.08 23-30 2 3 1.2
HBW600XCr35 600 3.0-5.5 1 1.0-3.0 0.06 0.06 30-40 1 1.5 1.2
HBW600XCr20Mo2Cu 600 3.0-5.5 1 1 0.06 0.06 18-21 1 1.4-2.0 0.8-1.2

2. Ni hard white Iron:

  • Handelsname Kurzzeichen W.St.Nr.
  • Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
  • Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
  • Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630
  • G-X 300 NiMo 15 3 0.9635
  • G-X 260 Cr 27 0.9635
ISO 21988/JN/ HBW C Si Mn P S Ni Cr
HBW480Cr2 480 2.5-3.0 0.8 0.8 0.1 0.1 3.0-5.5 1.5-3.0
HBW500Cr9 500 2.4-2.8 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0
HBW510Cr2 510 30.-3.6 0.8 0.8 0.1 0.1 3.0-5.5 1.5-3.0
HBW555Cr9 555 2.5-3.5 1.5-2.5 0.3-0.8 0.08 0.08 4.5-6.5 8.0-10.0
HBW630Cr9 630 3.2-3.6 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0

3. Martensitic Cr- Mo Alloy Steel: Hardness: ≥HRC48
4. Pearlitic Cr-Mo Alloy Steel Hardness: HB310-375
5. Heat-resistant Steel Plates.
6. High-temperature Alloy Plates.

Hardox Plates: HARDOX400, HARDOX450, HARDOX500, HARDOX550, HARDOX600, HARDOX630.
Bisplate:
BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600

Plate Thickness:
10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
Section Thickness: 1inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.

Feedback form contact with us
Related Product
AS2027 Cr15 Cement Mill Liner Plate Suppliers
AS2027 Cr15 Cement Mill Liner Plate Suppliers
Cement Mill Liner Plate Material Grade: AS2027 Cr15 Mill Type: Cement Mills + Raw Mills Production Process: Sand Process + Heattreatment Melting Process: Induction Melting Hardness: ≥ HRC56 Impact value: ≥5J Surface Finish: Appro.Ra100 Size Tolerance: as per CT13 ...
Learn More>
Chrome Molybdenum Steel Mine Mill Liners
Chrome Molybdenum Steel Mine Mill Liners
Chrome Molybdenum Steel Mine Mill Liners The Mine Mill Liners plates a huge role in the cement industry now, it is very helpful for us to improve work efficiency and skill level. Alloy: 15%Cr. The Mine Mill Liners Plates are cleaned, sandblasted with a nice surface without...
Learn More>
Product Catalog