Nickel Hard Ball Mill Lining and Liner Plates for Shot Blast Machines, Chutes, Clinker Silo, Port Machinery and Ball Mills This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.
These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining, Heat treatment shall be done.
The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur.
Plate Thickness is: 10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm,
80mm, 100mm, 200mm, 500mm, 1000mm.
Section Thickness is: 1 inch, 2 inch, 3 inch, 4 inch, 5 inch, 8 inch, 10 inch, 20 inch, 30 inch, 40 inch.
Material Grade is:
Cr-Mo Alloy Steel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo), high Cr white iron (BTMCr15Mo, BTMCr20Mo, BTMCr26Mo).

Our Ball Mill Lining Capability:

We can fabricate the Ni-hard Ball Mill Lining as per your material and your sizes.
We’d like to help select suitable material grade for your Ball Mill Lining as per your specific working condition.

Our Photos for Ball Mill Lining:

  • Ball Mill Lining
  • Ball Mill Lining
  • Ball Mill Lining
Q&A:

Q: Do you provide free samples?
A: Yes, usually we provide free samples for testing under the condition of freight paid by customer.

Q: What is the Warranty for our products ?
A: If any quality problems on our side occurred in this period , we will take on the shipping cost and replacement.

Q: What is the delivery time of your products?
A: It depends on the inventory availability.If items needed are in stock, the delivery time would be within 7 work days, but if not the delivery time would be around 30 work days.

Q: Can you manufacture Customization products?
A: Yes, we can.
We can produce both standard and special prosucts.
Our can make them according to your drawings and samples.
We will send working schedule of your order each week.
Our will inspect and test all merchandise in case of damaging and missing parts before shipment.

The detailed inspection picturesion by email.

Nickel Hard Ball Mill Lining Material Grades:

Reference Standard Nominal Chemical Composition (W%)
C Si Mn Cr Mo Ni P S
AS 2017/L2A 0.45-0.55 ≤0.75 0.50-1.00 0.80-1.20 - - ≤0.04 ≤0.04
AS 2017/L2B 0.55-0.65 ≤0.75 0.50-1.00 0.80-1.50 0.2-0.4 - ≤0.04 ≤0.04
AS 2017/L2C 0.70-0.90 ≤0.75 0.50-1.20 1.30-2.40 0.2-0.4 - ≤0.04 ≤0.04
ZG42Cr2Si2MnMo 0.38-0.48 1.5-1.8 0.8-1.2 1.8-2.2 0.2-0.6 - ≤0.04 ≤0.04
ZG45Cr2Mo 0.40-0.48 0.8-1.2 0.4-1.0 1.7-2.0 0.8-1.2 ≤0.5 ≤0.04 ≤0.04
ZG30Cr5Mo 0.25-0.35 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
ZG40Cr5Mo (FED-4A) 0.35-0.45 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
ZG50Cr5Mo 0.45-0.55 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
ZG60Cr5Mo 0.55-0.65 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
FMU-29 0.25-0.45 0.3-1.0 0.6-1.5 6.0-8.0 0.2-0.4 - ≤0.04 ≤0.04
FMU-11 0.90-1.30 0.3-1.0 0.6-1.5 11.0-13.0 0.3-0.5 - ≤0.04 ≤0.04
FMU-13 0.80-1.30 0.4-1.2 0.8-1.5 11.0-13.0 0.4-0.8 - ≤0.04 ≤0.04
FMU-14 1.60-2.00 0.4-1.2 0.8-1.5 11.0-13.0 0.6-1.0 - ≤0.04 ≤0.04
Ni-Hard Ball Mill Lining:

Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
Cast Iron Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
White Iron Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630

ISO 21988/JN/ HBW C Si Mn P S Ni Cr
HBW480Cr2 480 2.5-3.0 0.8 0.8 0.1 0.1 3.0-5.5 1.5-3.0
HBW500Cr9 500 2.4-2.8 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0
HBW510Cr2 510 30.-3.6 0.8 0.8 0.1 0.1 3.0-5.5 1.5-3.0
HBW555Cr9 555 2.5-3.5 1.5-2.5 0.3-0.8 0.08 0.08 4.5-6.5 8.0-10.0
HBW630Cr9 630 3.2-3.6 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0

Martensitic Cr- Mo Alloy Steel Hardness is ≥HRC484.

Pearlitic Cr-Mo Alloy Steel Hardness is HB310-375
Heat-resistant Steel Plates.
High-temperature Alloy Plates.
Hardox Plates include HARDOX400,HARDOX450, HARDOX500, HARDOX550, HARDOX600,HARDOX630.
Bisplate includes BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600